BASF Ultramid® B3S PA6 (尼龙6-聚酰胺) The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source! | |||
Physical Properties物理性质 | Metric公制数据 | English英制数据 | Comments测试方法 |
Density密度 | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
Water Absorption吸水率 | 9.0 - 10 % | 9.0 - 10 % | ISO 62 |
Moisture Absorption at Equilibrium吸湿平衡 | 2.6 - 3.4 % | 2.6 - 3.4 % | 23°C/50% R.H.; ISO 62 |
Viscosity Measurement粘度 | 145 | 145 | Viscosity Number; ISO 307 |
Linear Mold Shrinkage线性收缩率 | 0.0055 cm/cm | 0.0055 in/in | |
Melt Flow熔体流动速率 | 197.75 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | |
Mechanical Properties力学性能 | Metric公制数据 | English英制数据 | Comments测试方法 |
Tensile Strength, Yield屈服拉伸强度 | 90.0 MPa | 13100 psi | 50mm/min; ISO 527 |
Elongation at Yield屈服伸长率 | 4.0 % | 4.0 % | 50mm/min; ISO 527 |
Modulus of Elasticity弹性模量 | 3.40 GPa | 493 ksi | ISO 527 |
Flexural Modulus弯曲弹性模量 | 3.00 GPa | 435 ksi | ISO 178 |
Izod Impact, Notched悬臂梁缺口冲击强度(ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/A |
5.00 kJ/m² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ISO 180/A | |
Charpy Impact Unnotched夏比缺口试样冲击 | 25.0 J/cm² | 119 ft-lb/in² | ISO 179/1eU |
20.0 J/cm² @Temperature -30.0 °C | 95.2 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |
Charpy ImPAct, Notched夏比缺口冲击 | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
0.300 J/cm² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |
Electrical Properties电性能 | Metric公制数据 | English英制数据 | Comments测试方法 |
Volume ResiSTivity体积电阻率 | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
Dielectric Constant介电常数 | 3.3 @Frequency 1.00e+6 Hz | 3.3 @Frequency 1.00e+6 Hz | IEC 60250 |
Dissipation Factor耗散因数 | 0.030 @Frequency 1.00e+6 Hz | 0.030 @Frequency 1.00e+6 Hz | IEC 60250 |
Comparative Tracking Index跟踪指数 | 600 V | 600 V | Test Solution A; IEC 60112 |
Thermal Properties热性能 | Metric公制数据 | English英制数据 | Comments测试方法 |
CTE, linear, Parallel to Flow线性热膨胀系数 | 0.700 - 1.00 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.389 - 0.556 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 |
Specific Heat Capacity比热容 | 1.70 J/g-°C | 0.406 BTU/lb-°F | |
Thermal Conductivity导热系数 | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 |
Melting Point熔点 | 220 °C | 428 °F | DIN 53765 |
Maximum Service Temperature, Air最高使用温度 | 180 °C | 356 °F | |
Deflection Temperature at热变形温度0.46 MPa (66 psi) | 180 °C | 356 °F | ISO 75 |
Deflection Temperature at热变形温度1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75 |
Flammability, UL94阻燃等级 | V-2 @Thickness >=1.50 mm | V-2 @Thickness >=0.0591 in | |
Processing Properties加工性能 | Metric公制数据 | English英制数据 | Comments测试方法 |
Melt Temperature熔体温度 | 250 - 270 °C | 482 - 518 °F | Injection-molding/Extrusion |
Mold Temperature模具温度 | 40.0 - 60.0 °C | 104 - 140 °F | Injection-molding |