NIPPON PAPER SUPERCHLON®822S

产品详情

产品参数

1. Introduction:

Superchlon 822S is based on chlorinated polypropylene resin and is used as a primer for polypropylene materials. Polypropylene plastic has low weight, low cost, and excellent physical properties, chemical resistance, and heat resistance, making it widely used. However, its crystal structure and non-polar surface make adhesion difficult, limiting its application. However, Superchlon 822S can solve this problem because it has excellent adhesion to polypropylene plastics and topcoats made of polyurethane, acrylic, amino, epoxy, or alkyd resins. Superchlon 822S is commonly used as an adhesion promoter in polyolefin automotive bumper coatings. In addition, Superchlon 822S can also establish structural adhesion between polypropylene and other materials such as aluminum foil, fiber paper, polyester, and other plastics.

2. Specification: 20kg/box

Appearance: light yellow small pieces

Color (Gardner) 6 or below

Viscosity (25 ℃, Pas) 20-80 (20% solid content dissolved in toluene/isopropanol: 97/3)

Chlorine content 24.5 ± 1.0%

Molecular weight 40000-70000

Softening point 70-80 ℃

3. Solubility:

溶剂	溶解度	溶液外观
二甲苯	完全溶解	清澈
甲苯	完全溶解	清澈
环己烷	溶解	接近清澈
乙基环己烷	溶解	接近清澈
甲基环己烷	溶解	接近清澈
异丙醇	不溶解	沉淀

4. Compatibility:

Superchlon 822S mixed with other resins can enhance the adhesion between the primer and topcoat. Compared with traditional low chlorinated polyolefin resins, Superchlon 822S has been improved to enhance its adhesion to other resins. The following is the compatibility data between Superchlon 822S and other resins. Please note that if the proportion of other resins mixed is too high, it will reduce the adhesion to the polypropylene substrate. It is recommended that the proportion of other resins mixed should not exceed 30% by weight.

Compatibility with other resins

其它树脂	兼容性		树脂类型	生产商
	20% 甲苯溶液	漆膜
Paraloid A-11	○	○	热塑性丙烯酸	Rohm & Hass
Paraloid B-44	△	△	热塑性丙烯酸	Rohm & Hass
Paraloid B-66	x	x	热塑性丙烯酸	Rohm & Hass
Paraloid B-72	x	x	热塑性丙烯酸	Rohm & Hass
Dianal BR-102	x	x	热塑性丙烯酸	Mitsubushi Rayon
Cotax GX-059	○	○	热塑性丙烯酸	Toray Fine Chem
Laroflex MP-35	◎	◎	聚氯乙烯	BASF
Laroflex MP-45	◎	◎	聚氯乙烯	BASF
Evaflex-40	○	○	乙烯醋酸酯	Mitsui Polychem
Phthalkyd 355-50	◎	○	醇酸	Hitachi Chem
Phthalkyd 375	◎	◎	醇酸	Hitachi Chem
Phthalkyd V-902	◎	○	丙烯酸改性醇酸	Hitachi Chem
Phthalkyd V-903	△	○	丙烯酸改性醇酸	Hitachi Chem
Nisseki neopolymer 120	◎	○	石油树脂	Nihon Petrochem
Nisseki neopolymer 140	◎	○	石油树脂	Nihon Petrochem
Beckacite 1120	○	○	马林树脂	Nihon Reichoid
Pencell KK	◎	○	松香	Arakawa Chem
Tamanol 350	△	△	酚醛	Arakawa Chem
Lignol R-140	◎	○	二甲苯树脂	Lignite
Nikanol HP-70	◎	△	二甲苯树脂	Mitsubushi Gaschem

NOTE ◎---- 相容 ○---- 大部份相容 △---- 部份相容 x ---- 不相容

5. SUPERCHLON 822S heat sealing strength for various membranes:

Superchlon 822S is coated onto pre treated polypropylene film, left at room temperature for 10-15 minutes, heat sealed with various films, and tested for peel strength.

Experimental conditions:

-Heat sealing conditions: 100 ℃, 1kg/cm2, 1 sec

- 剥离测试: 15mm ，180°°，50mm/分钟

- 涂布量: 3g/㎡(干)

试验结果: